2008/9 Schools Wikipedia Selection. Related subjects: Chemical elements

13 magnesiumaluminiumsilicon


Periodic table - Extended periodic table
Name, symbol, number aluminium, Al, 13
Chemical series poor metals
Group, period, block 13,  3, p
Appearance silvery
Standard atomic weight 26.9815386 (13) g·mol−1
Electron configuration [Ne] 3s2 3p1
Electrons per shell 2, 8, 3
Physical properties
Phase solid
Density (near r.t.) 2.70 g·cm−3
Liquid density at m.p. 2.375 g·cm−3
Melting point 933.47  K
(660.32 ° C, 1220.58 ° F)
Boiling point 2792 K
(2519 ° C, 4566 ° F)
Heat of fusion 10.71 kJ·mol−1
Heat of vaporization 294.0 kJ·mol−1
Specific heat capacity (25 °C) 24.200 J·mol−1·K−1
Vapor pressure
P/Pa 1 10 100 1 k 10 k 100 k
at T/K 1482 1632 1817 2054 2364 2790
Atomic properties
Crystal structure face centered cubic
0.40494 nm
Oxidation states 3, 2 , 1
( amphoteric oxide)
Electronegativity 1.61 (Pauling scale)
Ionization energies
( more)
1st: 577.5 kJ·mol−1
2nd: 1816.7 kJ·mol−1
3rd: 2744.8 kJ·mol−1
Atomic radius 125 pm
Atomic radius (calc.) 118 pm
Covalent radius 118 pm
Magnetic ordering paramagnetic
Electrical resistivity (20 °C) 26.50 nΩ·m
Thermal conductivity (300 K) 237 W·m−1·K−1
Thermal expansion (25 °C) 23.1 µm·m−1·K−1
Speed of sound (thin rod) ( r.t.) (rolled) 5000  m·s−1
Young's modulus 70 GPa
Shear modulus 26 GPa
Bulk modulus 76 GPa
Poisson ratio 0.35
Mohs hardness 2.75
Vickers hardness 167 MPa
Brinell hardness 245 MPa
CAS registry number 7429-90-5
Selected isotopes
Main article: Isotopes of aluminium
iso NA half-life DM DE ( MeV) DP
26Al syn 7.17×105 y β+ 1.17 26Mg
ε - 26Mg
γ 1.8086 -
27Al 100% 27Al is stable with 14 neutrons

Aluminium (IPA: /ˌæljʊˈmɪniəm/, /ˌæljəˈmɪniəm/) or aluminium (/əˈluːmɪnəm/, see spelling below) is a silvery white and ductile member of the boron group of chemical elements. It has the symbol Al; its atomic number is 13. It is not soluble in water under normal circumstances. Aluminium is the most abundant metal in the Earth's crust, and the third most abundant element overall, after oxygen and silicon. It makes up about 8% by weight of the Earth’s solid surface. Aluminium is too reactive chemically to occur in nature as the free metal. Instead, it is found combined in over 270 different minerals. The chief source of aluminium is bauxite ore.

Aluminium is remarkable for its ability to resist corrosion (due to the phenomenon of passivation) and its light weight. Structural components made from aluminium and its alloys are vital to the aerospace industry and very important in other areas of transportation and building. Its reactive nature makes it useful as a catalyst or additive in chemical mixtures, including being used in ammonium nitrate explosives to enhance blast power.


Aluminium is a soft, lightweight, malleable metal with appearance ranging from silvery to dull gray, depending on the surface roughness. Aluminium is nontoxic, nonmagnetic, and nonsparking. It is also insoluble in alcohol, though it can be soluble in water only in certain forms. The yield strength of pure aluminium is 7–11 MPa, while aluminium alloys have yield strengths ranging from 200 MPa to 600 MPa. Aluminium has about one-third the density and stiffness of steel. It is ductile, and easily machined, cast, and extruded.

Corrosion resistance is excellent due to a thin surface layer of aluminium oxide that forms when the metal is exposed to air, effectively preventing further oxidation. The strongest aluminium alloys are less corrosion resistant due to galvanic reactions with alloyed copper.

Aluminium atoms are arranged in an face-centered cubic (FCC) structure. Aluminium has a high stacking-fault energy of approximately 200 mJ/m².

Aluminium is one of the few metals that retain full silvery reflectance in finely powdered form, making it an important component of silver paints. Aluminium mirror finish has the highest reflectance of any metal in the 200–400 nm (UV) and the 3000–10000 nm (far IR) regions, while in the 400–700 nm visible range it is slightly outdone by tin and silver and in the 700–3000 (near IR) by silver, gold, and copper.

Aluminium is a good thermal and electrical conductor, by weight better than copper. Aluminium is capable of being a superconductor, with a superconducting critical temperature of 1.2 kelvins and a critical magnetic field of about 100 gauss.


Aluminium has nine isotopes, whose mass numbers range from 23 to 30. Only 27Al ( stable isotope) and 26Al ( radioactive isotope, t1/2 = 7.2 × 105 y) occur naturally, however 27Al has a natural abundance of 99.9+ %. 26Al is produced from argon in the atmosphere by spallation caused by cosmic-ray protons. Aluminium isotopes have found practical application in dating marine sediments, manganese nodules, glacial ice, quartz in rock exposures, and meteorites. The ratio of 26Al to 10Be has been used to study the role of transport, deposition, sediment storage, burial times, and erosion on 105 to 106 year time scales. Cosmogenic 26Al was first applied in studies of the Moon and meteorites. Meteorite fragments, after departure from their parent bodies, are exposed to intense cosmic-ray bombardment during their travel through space, causing substantial 26Al production. After falling to Earth, atmospheric shielding protects the meteorite fragments from further 26Al production, and its decay can then be used to determine the meteorite's terrestrial age. Meteorite research has also shown that 26Al was relatively abundant at the time of formation of our planetary system. Most meteoriticists believe that the energy released by the decay of 26Al was responsible for the melting and differentiation of some asteroids after their formation 4.55 billion years ago.

Natural occurrence

In the Earth's crust, aluminium is the most abundant (8.13%) metallic element, and the third most abundant of all elements (after oxygen and silicon). However, because of its strong affinity to oxygen, it is not found in the elemental state but only in combined forms such as oxides or silicates. Aluminium is found in the lithosphere. The most common form it is found in is that of bauxite.

Production and refinement

Although aluminium is the most abundant metallic element in the Earth's crust (believed to be 7.5 to 8.1 percent), it is rare in its free form, occurring in oxygen-deficient environments such as volcanic mud, and it was once considered a precious metal more valuable than gold. Napoleon III, emperor of the French, is reputed to have given a banquet where the most honoured guests were given aluminium utensils, while the other guests had to make do with gold ones. Aluminium has been produced in commercial quantities for just over 100 years.

Aluminium is a strongly reactive metal that forms a high energy chemical bond with oxygen. Compared to most other metals, it is difficult to extract from ore, such as bauxite, due to the energy required to reduce aluminium oxide (Al2O3). For example, direct reduction with carbon, as is used to produce iron, is not chemically possible, since aluminium is a stronger reducing agent than carbon. Aluminium oxide has a melting point of about 2,000 °C. Therefore, it must be extracted by electrolysis. In this process, the aluminium oxide is dissolved in molten cryolite and then reduced to the pure metal. The operational temperature of the reduction cells is around 950 to 980 °C. Cryolite is found as a mineral in Greenland, but in industrial use it has been replaced by a synthetic substance. Cryolite is a chemical compound of aluminium, sodium, and calcium fluorides: (Na3AlF6). The aluminium oxide (a white powder) is obtained by refining bauxite in the Bayer process of Karl Bayer. (Previously, the Deville process was the predominant refining technology.)

The electrolytic process replaced the Wöhler process, which involved the reduction of anhydrous aluminium chloride with potassium. Both of the electrodes used in the electrolysis of aluminium oxide are carbon. Once the ore is in the molten state, its ions are free to move around. The reaction at the cathode — the negative terminal — is

Al3+ + 3 e → Al

Here the aluminium ion is being reduced (electrons are added). The aluminium metal then sinks to the bottom and is tapped off.

At the positive electrode ( anode), oxygen is formed:

2 O2− → O2 + 4 e

This carbon anode is then oxidized by the oxygen, releasing carbon dioxide. The anodes in a reduction cell must therefore be replaced regularly, since they are consumed in the process:

O2 + C → CO2

Unlike the anodes, the cathodes are not oxidized because there is no oxygen present at the cathode. The carbon cathode is protected by the liquid aluminium inside the cells. Nevertheless, cathodes do erode, mainly due to electrochemical processes. After five to ten years, depending on the current used in the electrolysis, a cell has to be rebuilt because of cathode wear.

World production trend of aluminium
World production trend of aluminium

Aluminium electrolysis with the Hall-Héroult process consumes a lot of energy, but alternative processes were always found to be less viable economically and/or ecologically. The world-wide average specific energy consumption is approximately 15±0.5 kilowatt-hours per kilogram of aluminium produced from alumina. (52 to 56 MJ/kg). The most modern smelters reach approximately 12.8 kW·h/kg (46.1 MJ/kg). (Compare this to the heat of reaction, 31 MJ/kg, and the Gibbs free energy of reaction, 29 MJ/kg.) Reduction line current for older technologies are typically 100 to 200 kA. State-of-the-art smelters operate with about 350 kA. Trials have been reported with 500 kA cells.

Recovery of the metal via recycling has become an important facet of the aluminium industry. Recycling involves melting the scrap, a process that uses only five percent of the energy needed to produce aluminium from ore. However, a significant part (up to 15% of input material) is lost as dross (ash-like oxide). Recycling was a low-profile activity until the late 1960s, when the growing use of aluminium beverage cans brought it to the public consciousness.

Electric power represents about 20% to 40% of the cost of producing aluminium, depending on the location of the smelter. Smelters tend to be situated where electric power is both plentiful and inexpensive, such as South Africa, the South Island of New Zealand, Australia, the People's Republic of China, the Middle East, Russia, Quebec and British Columbia in Canada, and Iceland.

Aluminium output in 2005
Aluminium output in 2005

In 2005, the People's Republic of China was the top producer of aluminium with almost one-fifth world share followed by Russia, Canada and USA reports the British Geological Survey.

Over the last 50 years, Australia has become a major producer of bauxite ore and a major producer and exporter of alumina. Australia produced 62 million tonnes of bauxite in 2005. The Australian deposits have some refining problems, some being high in silica but have the advantage of being shallow and relatively easy to mine.


Oxidation state one

  • AlH is produced when aluminium is heated in an atmosphere of hydrogen.
  • Al2O is made by heating the normal oxide, Al2O3, with silicon at 1800 °C in a vacuum.
  • Al2S can be made by heating Al2S3 with aluminium shavings at 1300 °C in a vacuum. It quickly disproportionates to the starting materials. The selenide is made in a parallel manner.
  • AlF, AlCl and AlBr exist in the gaseous phase when the tri-halide is heated with aluminium.

Aluminium halides usually exist in the form AlX3. e.g. AlF3, AlCl3, AlBr3, AlI3 etc.

Oxidation state two

  • Aluminium monoxide, AlO, is present when aluminium powder burns in oxygen.

Oxidation state three

  • Fajans' rules show that the simple trivalent cation Al3+ is not expected to be found in anhydrous salts or binary compounds such as Al2O3. The hydroxide is a weak base and aluminium salts of weak acids, such as carbonate, can't be prepared. The salts of strong acids, such as nitrate, are stable and soluble in water, forming hydrates with at least six molecules of water of crystallization.
  • Aluminium hydride, (AlH3)n, can be produced from trimethylaluminium and an excess of hydrogen. It burns explosively in air. It can also be prepared by the action of aluminium chloride on Lithium hydride">lithium hydride in ether solution, but cannot be isolated free from the solvent.
  • Aluminium carbide, Al4C3 is made by heating a mixture of the elements above 1000 °C. The pale yellow crystals have a complex lattice structure, and react with water or dilute acids to give methane. The acetylide, Al2(C2)3, is made by passing acetylene over heated aluminium.
  • Aluminium nitride, AlN, can be made from the elements at 800 °C. It is hydrolysed by water to form ammonia and aluminium hydroxide.
  • Aluminium phosphide, AlP, is made similarly, and hydrolyses to give phosphine.
  • Aluminium oxide, Al2O3, occurs naturally as corundum, and can be made by burning aluminium in oxygen or by heating the hydroxide, nitrate or sulfate. As a gemstone, its hardness is only exceeded by diamond, boron nitride, and carborundum. It is almost insoluble in water.
  • Aluminium hydroxide may be prepared as a gelatinous precipitate by adding ammonia to an aqueous solution of an aluminium salt. It is amphoteric, being both a very weak acid, and forming aluminates with alkalis. It exists in various crystalline forms.
  • Aluminium sulfide, Al2S3, may be prepared by passing hydrogen sulfide over aluminium powder. It is polymorphic.
  • Aluminium iodide, (AlI3)2, is a dimer with applications in organic synthesis.
  • Aluminium fluoride, AlF3, is made by treating the hydroxide with HF, or can be made from the elements. It consists of a giant molecule which sublimes without melting at 1291 °C. It is very inert. The other trihalides are dimeric, having a bridge-like structure.
  • Aluminium fluoride/water complexes: When aluminium and fluoride are together in aqueous solution, they readily form complex ions such as AlF(H2O)5+2, AlF3(H2O)30, AlF6-3. Of these, AlF6-3 is the most stable. This is explained by the fact that aluminium and fluoride, which are both very compact ions, fit together just right to form the octahedral aluminium hexafluoride complex. When aluminium and fluoride are together in water in a 1:6 molar ratio, AlF6-3 is the most common form, even in rather low concentrations.
  • Organo-metallic compounds of empirical formula AlR3 exist and, if not also giant molecules, are at least dimers or trimers. They have some uses in organic synthesis, for instance trimethylaluminium.
  • Alumino-hydrides of the most electropositive elements are known, the most useful being lithium aluminium hydride, Li[AlH4]. It decomposes into lithium hydride, aluminium and hydrogen when heated, and is hydrolysed by water. It has many uses in organic chemistry, particularly as a reducing agent. The aluminohalides have a similar structure.


In the journal Science of 14 January 2005 it was reported that clusters of 13 aluminium atoms (Al13) had been made to behave like an iodine atom; and, 14 aluminium atoms (Al14) behaved like an alkaline earth atom. The researchers also bound 12 iodine atoms to an Al13 cluster to form a new class of polyiodide. This discovery is reported to give rise to the possibility of a new characterisation of the periodic table: superatoms. The research teams were led by Shiv N. Khanna ( Virginia Commonwealth University) and A. Welford Castleman Jr ( Penn State University).


General use

A piece of aluminium metal.
A piece of aluminium metal.

Aluminium is the most widely used non-ferrous metal. Global production of aluminium in 2005 was 31.9 million tonnes. It exceeded that of any other metal except iron (837.5 million tonnes). Relatively pure aluminium is encountered only when corrosion resistance and/or workability is more important than strength or hardness. A thin layer of aluminium can be deposited onto a flat surface by physical vapor deposition or (very infrequently) chemical vapor deposition or other chemical means to form optical coatings and mirrors. When so deposited, a fresh, pure aluminium film serves as a good reflector (approximately 92%) of visible light and an excellent reflector (as much as 98%) of medium and far infrared.

Pure aluminium has a low tensile strength, but when combined with thermo-mechanical processing, aluminium alloys display a marked improvement in mechanical properties, especially when tempered. Aluminium alloys form vital components of aircraft and rockets as a result of their high strength-to-weight ratio. Aluminium readily forms alloys with many elements such as copper, zinc, magnesium, manganese and silicon (e.g., duralumin). Today, almost all bulk metal materials that are referred to loosely as "aluminium," are actually alloys. For example, the common aluminium foils are alloys of 92% to 99% aluminium.

Some of the many uses for aluminium metal are in:

household aluminium foil
household aluminium foil
  • Transportation (automobiles, aircraft, trucks, railway cars, marine vessels, bicycles etc.)
  • Packaging ( cans, foil, etc.)
  • Water treatment
  • Treatment against fish parasites such as Gyrodactylus salaris.
  • Construction ( windows, doors, siding, building wire, etc.)
  • Cooking utensils
  • Electrical transmission lines for power distribution
  • MKM steel and Alnico magnets
  • Super purity aluminium (SPA, 99.980% to 99.999% Al), used in electronics and CDs.
  • Heat sinks for electronic appliances such as transistors and CPUs.
  • Powdered aluminium is used in paint, and in pyrotechnics such as solid rocket fuels and thermite.
  • In the blades of prop swords and knives used in stage combat.
  • Aluminium is widely used in watch production as it provides durability and resists tarnishing and corrosion.

Aluminium compounds

  • Aluminium ammonium sulfate ([Al(NH4)](SO4)2), ammonium alum is used as a mordant, in water purification and sewage treatment, in paper production, as a food additive, and in leather tanning.
  • Aluminium acetate is a salt used in solution as an astringent.
  • Aluminium borate (Al2O3 B2O3) is used in the production of glass and ceramic.
  • Aluminium borohydride (Al(BH4)3) is used as an additive to jet fuel.
  • Aluminium chlorohydride is used as an antiperspirant and in the treatment of hyperhidrosis.
  • Aluminium fluorosilicate (Al2(SiF6)3) is used in the production of synthetic gemstones, glass and ceramic.
  • Aluminium hydroxide (Al(OH)3) is used: as an antacid, as a mordant, in water purification, in the manufacture of glass and ceramic and in the waterproofing of fabrics.
  • Aluminium oxide (Al2O3), alumina, is found naturally as corundum ( rubies and sapphires), emery, and is used in glass making. Synthetic ruby and sapphire are used in lasers for the production of coherent light.
  • Aluminium phosphate (AlPO4) is used in the manufacture: of glass and ceramic, pulp and paper products, cosmetics, paints and varnishes and in making dental cement.
  • Aluminium sulfate (Al2(SO4)3) is used: in the manufacture of paper, as a mordant, in a fire extinguisher, in water purification and sewage treatment, as a food additive, in fireproofing, and in leather tanning.
  • In many vaccines, certain aluminium salts serve as an immune adjuvant (immune response booster) to allow the protein in the vaccine to achieve sufficient potency as an immune stimulant.

Aluminium alloys in structural applications

Aluminium foam
Aluminium foam

Aluminium alloys with a wide range of properties are used in engineering structures. Alloy systems are classified by a number system ( ANSI) or by names indicating their main alloying constituents ( DIN and ISO).

The strength and durability of aluminium alloys vary widely, not only as a result of the components of the specific alloy, but also as a result of heat treatments and manufacturing processes. A lack of knowledge of these aspects has from time to time led to improperly designed structures and gained aluminium a bad reputation. (See main article)

One important structural limitation of aluminium alloys is their fatigue strength. Unlike steels, aluminium alloys have no well-defined fatigue limit, meaning that fatigue failure will eventually occur under even very small cyclic loadings. This implies that engineers must assess these loads and design for a fixed life rather than an infinite life.

Another important property of aluminium alloys is their sensitivity to heat. Workshop procedures involving heating are complicated by the fact that aluminium, unlike steel, will melt without first glowing red. Forming operations where a blow torch is used therefore requires some expertise, since no visual signs reveal how close the material is to melting. Aluminium alloys, like all structural alloys, also are subject to internal stresses following heating operations such as welding and casting. The problem with aluminium alloys in this regard is their low melting point, which make them more susceptible to distortions from thermally induced stress relief. Controlled stress relief can be done during manufacturing by heat-treating the parts in an oven, followed by gradual cooling -- in effect annealing the stresses.

The low melting point of aluminium alloys has not precluded their use in rocketry; even for use in constructing combustion chambers where gases can reach 3500 K. The Agena upper stage engine used a regeneratively cooled aluminium design for some parts of the nozzle, including the thermally critical throat region.

Household wiring

Aluminium has about 65% of the conductivity of copper, the traditional household wiring material. In the 1960s aluminium was considerably cheaper than copper, and so was introduced for household electrical wiring in the United States, even though many fixtures had not been designed to accept aluminium wire. However, in some cases the greater coefficient of thermal expansion of aluminium causes the wire to expand and contract relative to the dissimilar metal screw connection, eventually loosening the connection. Also, pure aluminium has a tendency to creep under steady sustained pressure (to a greater degree as the temperature rises), again loosening the connection. Finally, Galvanic corrosion from the dissimilar metals increased the electrical resistance of the connection.

All of this resulted in overheated and loose connections, and this in turn resulted in fires. Builders then became wary of using the wire, and many jurisdictions outlawed its use in very small sizes in new construction. Eventually, newer fixtures were introduced with connections designed to avoid loosening and overheating. At first they were marked "Al/Cu", but they now bear a "CO/ALR" coding. In older assemblies, workers forestall the heating problem using a properly-done crimp of the aluminium wire to a short " pigtail" of copper wire. Today, new alloys, designs, and methods are used for aluminium wiring in combination with aluminium terminations.


Ancient Greeks and Romans used aluminium salts as dyeing mordants and as astringents for dressing wounds; alum is still used as a styptic. In 1761 Guyton de Morveau suggested calling the base alum alumine. In 1808, Humphry Davy identified the existence of a metal base of alum, which he at first termed alumium and later aluminium (see Etymology section, below).

The statue of the Angel of Christian Charity (commonly mistaken for Eros) in Piccadilly Circus London, was made in 1893 and is one of the first statues to be cast in aluminium.
The statue of the Angel of Christian Charity (commonly mistaken for Eros) in Piccadilly Circus London, was made in 1893 and is one of the first statues to be cast in aluminium.

Friedrich Wöhler is generally credited with isolating aluminium (Latin alumen, alum) in 1827 by mixing anhydrous aluminium chloride with potassium. As the metal had first been produced two years earlier (in an impure form) by Danish physicist and chemist Hans Christian Ørsted, Ørsted can also be listed as its discoverer. Further, Pierre Berthier discovered aluminium in bauxite ore and successfully extracted it. Frenchman Henri Etienne Sainte-Claire Deville improved Wöhler's method in 1846, and described his improvements in a book in 1859, chief among these being the substitution of sodium for the considerably more expensive potassium.

(Note: The title of Deville's book is "De l'aluminium, ses propriétés, sa fabrication" (Paris, 1859). Deville likely also conceived the idea of the electrolysis of aluminium oxide dissolved in cryolite; however, Charles Martin Hall and Paul Héroult might have developed the more practical process after Deville.)

Before the Hall-Héroult process was developed, aluminium was exceedingly difficult to extract from its various ores. This made pure aluminium more valuable than gold. Bars of aluminium were exhibited alongside the French crown jewels at the Exposition Universelle of 1855, and Napoleon III was said to have reserved a set of aluminium dinner plates for his most honored guests.

Aluminium was selected as the material to be used for the apex of the Washington Monument in 1884, a time when one ounce (30 grams) cost the daily wage of a common worker on the project; aluminium was about the same value as silver.

The Cowles companies supplied aluminium alloy in quantity in the United States and England using smelters like the furnace of Carl Wilhelm Siemens by 1886. Charles Martin Hall of Ohio in the U.S. and Paul Héroult of France independently developed the Hall-Héroult electrolytic process that made extracting aluminium from minerals cheaper and is now the principal method used worldwide. The Hall-Heroult process cannot produce Super Purity Aluminium directly. Hall's process, in 1888 with the financial backing of Alfred E. Hunt, started the Pittsburgh Reduction Company today known as Alcoa. Héroult's process was in production by 1889 in Switzerland at Aluminium Industrie, now Alcan, and at British Aluminium, now Luxfer Group and Alcoa, by 1896 in Scotland.

By 1895 the metal was being used as a building material as far away as Sydney, Australia in the dome of the Chief Secretary's Building.

In November 2007 the price of aluminium on NYMEX was around $1.10 or $1.20 a pound.


Nomenclature history

The earliest citation given in the Oxford English Dictionary for any word used as a name for this element is alumium, which Humphry Davy employed in 1808 for the metal he was trying to isolate electrolytically from the mineral alumina. The citation is from his journal Philosophical Transactions: "Had I been so fortunate have procured the metallic substances I was in search of, I should have proposed for them the names of silicium, alumium, zirconium, and glucium."

By 1812, Davy had settled on aluminium, which, as other sources note, matches its Latin root. He wrote in the journal Chemical Philosophy: "As yet Aluminium has not been obtained in a perfectly free state." But the same year, an anonymous contributor to the Quarterly Review, a British political-literary journal, objected to aluminium and proposed the name aluminium, "for so we shall take the liberty of writing the word, in preference to aluminium, which has a less classical sound."

The -ium suffix had the advantage of conforming to the precedent set in other newly discovered elements of the time: potassium, sodium, magnesium, calcium, and strontium (all of which Davy had isolated himself). Nevertheless, -um spellings for elements were not unknown at the time, as for example platinum, known to Europeans since the sixteenth century, molybdenum, discovered in 1778, and tantalum, discovered in 1802.

Americans adopted -ium to fit the standard form of the periodic table of elements, for most of the nineteenth century, with aluminium appearing in Webster's Dictionary of 1828. In 1892, however, Charles Martin Hall used the -um spelling in an advertising handbill for his new electrolytic method of producing the metal, despite his constant use of the -ium spelling in all the patents he filed between 1886 and 1903. It has consequently been suggested that the spelling reflects an easier to pronounce word with one fewer syllable, or that the spelling on the flier was a mistake. Hall's domination of production of the metal ensured that the spelling aluminium became the standard in North America; the Webster Unabridged Dictionary of 1913, though, continued to use the -ium version.

In 1926, the American Chemical Society officially decided to use aluminium in its publications; American dictionaries typically label the spelling aluminium as a British variant.

Present-day spelling

In the UK and other countries using British spelling, only aluminium is used. In the United States, the spelling aluminium is largely unknown, and the spelling aluminium predominates. The Canadian Oxford Dictionary prefers aluminium, whereas the Australian Macquarie Dictionary prefers aluminium. The spelling in virtually all other languages is analogous to the -ium ending.

The International Union of Pure and Applied Chemistry (IUPAC) adopted Aluminium as the standard international name for the element in 1990, but three years later recognized aluminium as an acceptable variant. Hence their periodic table includes both, but places aluminium first. IUPAC officially prefers the use of Aluminium in its internal publications, although several IUPAC publications use the spelling aluminium.

Biological role


The toxicity of aluminium can be traced to increased deposition in bone and the central nervous system, particularly in the presence of reduced renal function. Because aluminium competes with calcium for absorption, increased amounts of dietary aluminium may contribute to the reduced skeletal mineralization (osteopenia) observed in preterm infants and infants with growth retardation. Full-term infants with normal renal function do not seem to be at substantial risk from aluminium toxicity from soy protein-based formulas. Aluminium can cause neurotoxicity in very high doses which can alter the function of the blood-brain barrier. It is one of the few abundant elements that have no known function in living cells. A small percentage of people are allergic to it — they experience contact dermatitis: an itchy rash from using styptic or antiperspirant products, digestive disorders and inability to absorb nutrients from eating food cooked in aluminium pans, and vomiting and other symptoms of poisoning from ingesting such products as Amphojel, and Maalox (antacids). Such allergies are extremely rare though, in other people aluminium is not considered as toxic as heavy metals, but there is evidence of some toxicity if it is consumed in excessive amounts. The use of aluminium cookware, popular because of its corrosion resistance and good heat conduction, has not been shown to lead to aluminium toxicity in general. Excessive consumption of antacids containing aluminium compounds and excessive use of aluminium-containing antiperspirants are more likely causes of toxicity. Aluminium increases estrogen-related gene expression in human breast cancer cells grown in the laboratory. These salts' estrogen-like effects have led to their classification as a metalloestrogen.

It has been suggested that aluminium is a cause of Alzheimer's disease, as some brain plaques have been found to contain the metal. Research in this area has been inconclusive; aluminium accumulation may be a consequence of the Alzheimer's damage, not the cause. In any event, if there is any toxicity of aluminium it must be via a very specific mechanism, since total human exposure to the element in the form of naturally occurring clay in soil and dust is enormously large over a lifetime.

Mercury applied to the surface of an aluminium alloy can damage the protective oxide surface film by forming amalgam. This may cause further corrosion and weakening of the structure. For this reason, mercury thermometers are not allowed on many airliners, as aluminium is used in many aircraft structures.

A mixture of powdered aluminium and Fe2O3 is known as thermite, and burns with a high energy output to form Fe and Al2O3. Thermite can be produced inadvertently during grinding operations, but the high ignition temperature makes incidents unlikely in most workshop environments.

Retrieved from ""
This Wikipedia Selection has a sponsor: SOS Children , and consists of a hand selection from the English Wikipedia articles with only minor deletions (see for details of authors and sources). The articles are available under the GNU Free Documentation License. See also our Disclaimer.